Tenax Eliox Knife Grade Epoxy- Part A & B

Tenax Eliox is an extra clear bi-component epoxy knife grade glue approved for food contact. Suitable to fill, glue and laminate marble, stone, granite, quartz and ceramic. Can be used indoor and outdoor with low yellowing. This product is extra clear, soft and light, easy to spread and with a high gloss and brightness.

In compliance with Legislative Decree no. 29/2017 the mastic is approved for food contact*. The mastic has low smell and also present low risk phrases, no toxic to long term, for the health of the final user. ELIOX has also LOW content of VOC.

Features

Excellent adhesion
Very low shrinkage during the hardening processing
Easy to color
Soft and easy to apply
Very bright and easy to polish
Dripless and does not sag
Resistant to temperature
Indoor/Outdoor
Extra strong
Transparent
Extra clear
Very low yellowing
Very easy dosing
Food contact approved

What's Included

Part A - 1.5 kg
Part B - 0.75 kg

Technical Data

Tenax Eliox Knife Grade Epoxy
Viscosity part A / part B cps 25°C :	Tixotropic paste / Tixotropic paste
Density part A / part B at 25°C gr/cm³ :	1.1 / 1.0
Mixing Ratio hardener :	100+50
Ratio of use glue/hardener:	100+2/3
Gel time in bulk at 25°C :	10-15 min
Tacky free in thin layer at 25° C in min :	Approx. 3h – 3h 30min
Working time suggested at 25°c in min:	Approx. 60-70 min
Hardeness in Shore D ASTM D 2240 :	80
Minimum temperature of use after hardening:	0°C
Yellowing test in climatic chamber Qsun, (ASTM D904), 1 year of outdoor conditions, light + rain+ thermal shock :	Low
Minimum reaction temperature :	+10°C
Minimum temperature of use after hardening :	-25°C
Maximum temperature of use after hardening :	+60°C
Working time at 25°C (time for polishing or cutting) :	24 hours
Adhesion on marble after 8h :	11 MPa
Adhesion on marble after 24h :	12 MPa
Adhesion on quartz after 8h :	13 MPa
Adhesion on quartz after 24h :	13 MPa
Adhesion on ceramic after 8h :	16 MPa
Adhesion on ceramic after 24h :	17 MPa